Chemical composition Element Mass percent Element Mass percent Si 0.20–0.8 Fe 0.7 Cu 3.5–4.5 Mn 0.40–1.0 Mg 0.40–0.8 Cr 0.10 Zn 0.25 Ti 0.15 Additional — Others each / total 0.05 / 0.15 Al Remainder

Mechanical properties by temper Temper Wall mm UTS MPa Yield MPa Elongation % O All in supplier table ≤245 ≤125 ≥16 T4 All in supplier table ≥345 ≥215 ≥12 T1 All in supplier table ≥335 ≥195 ≥12

Application areas Mechanical control rods and linkages Machined tubular parts and sleeves Legacy aerospace components to qualified drawings

Chemical composition Element Mass percent Element Mass percent Si 0.20–0.8 Fe 0.7 Cu 3.5–4.5 Mn 0.40–1.0 Mg 0.40–0.8 Cr 0.10 Zn 0.25 Ti 0.15 Additional — Others each / total 0.05 / 0.15 Al Remainder

Mechanical properties by temper Temper Wall mm UTS MPa Yield MPa Elongation % O All in supplier table ≤245 ≤125 ≥16 T4 All in supplier table ≥345 ≥215 ≥12 T1 All in supplier table ≥335 ≥195 ≥12

Application areas Mechanical control rods and linkages Machined tubular parts and sleeves Legacy aerospace components to qualified drawings

2017 Aluminum Tube/Pipe

Grade: 2017

Size:

Extruded: 6mm*1mm-400mm*40mm

Seamless: 70mm*10mm-270mm*60mm

Forged: 120mm*20mm-1200mm*200mm

Standard: ASTM, AMS, BS etc.

2017 is a heat treatable aluminum copper magnesium silicon alloy, commonly supplied in the naturally aged T4 condition. It combines useful strength with machinability and can serve tubular mechanical components and control linkages. Corrosion protection is normally required in aggressive environments, and fusion welding requires careful qualification. Tube availability and specification coverage are more limited than for 2024. The distinct designation 2017A must not be substituted without checking composition, mechanical requirements and customer approval.

Chemical composition

Element	Mass percent	Element	Mass percent
Si	0.20–0.8	Fe	0.7
Cu	3.5–4.5	Mn	0.40–1.0
Mg	0.40–0.8	Cr	0.10
Zn	0.25	Ti	0.15
Additional	—	Others each / total	0.05 / 0.15
Al	Remainder

Mechanical properties by temper

Temper	Wall mm	UTS MPa	Yield MPa	Elongation %
O	All in supplier table	≤245	≤125	≥16
T4	All in supplier table	≥345	≥215	≥12
T1	All in supplier table	≥335	≥195	≥12

Application areas

Mechanical control rods and linkages
Machined tubular parts and sleeves
Legacy aerospace components to qualified drawings

Introduction

Specification

Chemical composition

Element	Mass percent	Element	Mass percent
Si	0.20–0.8	Fe	0.7
Cu	3.5–4.5	Mn	0.40–1.0
Mg	0.40–0.8	Cr	0.10
Zn	0.25	Ti	0.15
Additional	—	Others each / total	0.05 / 0.15
Al	Remainder

Mechanical

Mechanical properties by temper

Temper	Wall mm	UTS MPa	Yield MPa	Elongation %
O	All in supplier table	≤245	≤125	≥16
T4	All in supplier table	≥345	≥215	≥12
T1	All in supplier table	≥335	≥195	≥12