Chemical composition Element Limit wt % Element Limit wt % Si 0.60 max Fe 0.70 max Cu 0.05–0.20 Mn 1.00–1.50 Mg — Cr — Zn 0.10 max Ti — Other each 0.05 max Other total 0.15 max Al Balance

Mechanical properties by temper Temper Thickness mm Rm MPa Rp0.2 MPa Elongation % O 1.5–3.0 95–135 35 min 20 min H14 1.5–3.0 145–185 125 min 3 min H24 1.5–3.0 145–185 125 min 5 min H18 1.5–3.0 190 min 170 min 2 min

Application areas Heat exchangers and formed thermal components Ductwork and general sheet metal fabrication Cooking utensils and drawn or spun parts Roofing siding gutters and downspouts Compatible chemical equipment and storage tanks

Chemical composition Element Limit wt % Element Limit wt % Si 0.60 max Fe 0.70 max Cu 0.05–0.20 Mn 1.00–1.50 Mg — Cr — Zn 0.10 max Ti — Other each 0.05 max Other total 0.15 max Al Balance

Mechanical properties by temper Temper Thickness mm Rm MPa Rp0.2 MPa Elongation % O 1.5–3.0 95–135 35 min 20 min H14 1.5–3.0 145–185 125 min 3 min H24 1.5–3.0 145–185 125 min 5 min H18 1.5–3.0 190 min 170 min 2 min

Application areas Heat exchangers and formed thermal components Ductwork and general sheet metal fabrication Cooking utensils and drawn or spun parts Roofing siding gutters and downspouts Compatible chemical equipment and storage tanks

3003 Aluminum Sheet and Plate

Grade: 3003

Coil: 0.3mm-3.0mm

Sheet: 0.3mm-300mm

Width: 50mm-2000mm

Standard: ASTM, AMS, BS etc.

3003 is a wrought aluminum manganese alloy widely supplied as sheet, coil and plate. It provides moderate strength with good corrosion resistance, weldability and forming ability. Strength is developed by cold working rather than precipitation heat treatment. Annealed material supports drawing and spinning, while H14 and H24 offer greater handling strength. Typical uses include fabricated sheet components, heat exchangers and building products. Selection is usually driven by ease of fabrication and corrosion performance rather than high structural loading.

Chemical composition

Element	Limit wt %	Element	Limit wt %
Si	0.60 max	Fe	0.70 max
Cu	0.05–0.20	Mn	1.00–1.50
Mg	—	Cr	—
Zn	0.10 max	Ti	—
Other each	0.05 max	Other total	0.15 max
Al	Balance

Mechanical properties by temper

Temper	Thickness mm	Rm MPa	Rp0.2 MPa	Elongation %
O	1.5–3.0	95–135	35 min	20 min
H14	1.5–3.0	145–185	125 min	3 min
H24	1.5–3.0	145–185	125 min	5 min
H18	1.5–3.0	190 min	170 min	2 min

Application areas

Heat exchangers and formed thermal components
Ductwork and general sheet metal fabrication
Cooking utensils and drawn or spun parts
Roofing siding gutters and downspouts
Compatible chemical equipment and storage tanks

Introduction

Specification

Chemical composition

Element	Limit wt %	Element	Limit wt %
Si	0.60 max	Fe	0.70 max
Cu	0.05–0.20	Mn	1.00–1.50
Mg	—	Cr	—
Zn	0.10 max	Ti	—
Other each	0.05 max	Other total	0.15 max
Al	Balance

Mechanical

Mechanical properties by temper

Temper	Thickness mm	Rm MPa	Rp0.2 MPa	Elongation %
O	1.5–3.0	95–135	35 min	20 min
H14	1.5–3.0	145–185	125 min	3 min
H24	1.5–3.0	145–185	125 min	5 min
H18	1.5–3.0	190 min	170 min	2 min