Chemical Composition (wt.%): Iron, Fe 49 Nickel, Ni 48 Cobalt, Co 1 Manganese, Mn 0.80 Silicon, Si 0.30 Chromium, Cr 0.25 Aluminum, Al 0.10 Carbon, C 0.050 Phosphorous, P 0.025 Sulfur, S 0.025

Mechanical Properties: Material Ultimate Tensile Strength Yield Strength 0.2 % Elongation (%) psi MPa psi MPa Alloy 48 75,000 520 38,000 260 43

Applications: Glass seals Electronic packages Optical devices

Chemical Composition (wt.%): Iron, Fe 49 Nickel, Ni 48 Cobalt, Co 1 Manganese, Mn 0.80 Silicon, Si 0.30 Chromium, Cr 0.25 Aluminum, Al 0.10 Carbon, C 0.050 Phosphorous, P 0.025 Sulfur, S 0.025

Mechanical Properties: Material Ultimate Tensile Strength Yield Strength 0.2 % Elongation (%) psi MPa psi MPa Alloy 48 75,000 520 38,000 260 43

Applications: Glass seals Electronic packages Optical devices

Alloy 48 / UNS K94800

Grade: Alloy 48 / UNS K94800 / Nilo 48

Sheet/Plate: 0.3mm-150mm

Strip/Foil: 0.02mm-16mm

Pipe: 6mm*0.5mm-1200mm*100mm

Bar: Ф6mm – Ф600mm

Wire: Ф0.01mm – Ф6mm

Others: Forged Rings, Flanges, Elbows, Tees, Reducers etc.

Standard: ASTM/ASME/AMS

UNS K94800/Nilo 48/Alloy 48
Alloy 48 (Nilo 48) is a nickel-iron controlled-expansion alloy containing 48% nickel. Alloy 48 (Nilo 48 coefficient of thermal expansion matches that of soft lead and soda lime glasses therefore Alloy 48′s main use is for glass to metal seals in soft lead or soda lime type glasses. Alloy 48 is also used for thermostats in industrial applications up to 450°C (840°F).

Chemical Composition (wt.%):