XM-13/13-8MoPH Stainless Steel Plate
Grade: XM-13/13-8MoPH
Thickness: 3.0mm-200mm
Width: 1.5m/2.0m/2.2m or as client’s requirement.
Standard: ASTM A240/A240M, JIS G4304, JISG 4305, EN 10088/3
Finish: No.1, Polished
- Fast Shipping / Ready Stock
- ISO 9001 Direct Factory
- Custom Cutting & Processing
- 100% MTC & SGS Inspection Supported
XM-13 (13-8MoPH, UNS S13800) is a high-strength precipitation hardening stainless steel with excellent toughness, stress corrosion cracking resistance, and dimensional stability.
Chemical Composition (Typical wt.%)
| Element | Value |
| Carbon (C) | ≤0.05 |
| Chromium (Cr) | 12.25-13.25 |
| Nickel (Ni) | 7.50-8.50 |
| Molybdenum (Mo) | 2.00-2.50 |
| Aluminum (Al) | 0.90-1.35 |
Mechanical Properties (Typical Condition)
| Property | Value |
| Tensile Strength | ≥1380 MPa |
| Yield Strength | ≥1280 MPa |
| Hardness | Up to 45 HRC |
- Aerospace structures
- Aircraft fittings
- Oil and gas components
- High-strength parts
XM-13 (13-8MoPH, UNS S13800) is a high-strength precipitation hardening stainless steel with excellent toughness, stress corrosion cracking resistance, and dimensional stability.
Chemical Composition (Typical wt.%)
| Element | Value |
| Carbon (C) | ≤0.05 |
| Chromium (Cr) | 12.25-13.25 |
| Nickel (Ni) | 7.50-8.50 |
| Molybdenum (Mo) | 2.00-2.50 |
| Aluminum (Al) | 0.90-1.35 |
Mechanical Properties (Typical Condition)
| Property | Value |
| Tensile Strength | ≥1380 MPa |
| Yield Strength | ≥1280 MPa |
| Hardness | Up to 45 HRC |
- Aerospace structures
- Aircraft fittings
- Oil and gas components
- High-strength parts