632/15-7MoPH Stainless Steel Plate
Grade: 632/15-7MoPH
Thickness: 3.0mm-200mm
Width: 1.5m/2.0m/2.2m or as client’s requirement.
Standard: ASTM A240/A240M, JIS G4304, JISG 4305, EN 10088/3
Finish: No.1, Polished
- Fast Shipping / Ready Stock
- ISO 9001 Direct Factory
- Custom Cutting & Processing
- 100% MTC & SGS Inspection Supported
632 (15-7MoPH, UNS S15700) is a precipitation hardening stainless steel containing molybdenum, providing high strength, corrosion resistance, and good fatigue properties.
Chemical Composition (Typical wt.%)
| Element | Value |
| Carbon (C) | ≤0.09 |
| Chromium (Cr) | 14.00-16.00 |
| Nickel (Ni) | 6.50-7.75 |
| Molybdenum (Mo) | 2.00-3.00 |
| Aluminum (Al) | 0.75-1.50 |
Mechanical Properties (Typical Condition)
| Property | Value |
| Tensile Strength | ≥1200 MPa |
| Yield Strength | ≥1000 MPa |
| Hardness | Up to 45 HRC |
- Aerospace components
- Springs
- Aircraft structures
- High-strength parts
632 (15-7MoPH, UNS S15700) is a precipitation hardening stainless steel containing molybdenum, providing high strength, corrosion resistance, and good fatigue properties.
Chemical Composition (Typical wt.%)
| Element | Value |
| Carbon (C) | ≤0.09 |
| Chromium (Cr) | 14.00-16.00 |
| Nickel (Ni) | 6.50-7.75 |
| Molybdenum (Mo) | 2.00-3.00 |
| Aluminum (Al) | 0.75-1.50 |
Mechanical Properties (Typical Condition)
| Property | Value |
| Tensile Strength | ≥1200 MPa |
| Yield Strength | ≥1000 MPa |
| Hardness | Up to 45 HRC |
- Aerospace components
- Springs
- Aircraft structures
- High-strength parts