Product Description

Inconel 600

Inconel 600

•good resistance to oxidation, carburization and nitridation
•good resistance to stress corrosion cracking, at both room and elevated temperatures
•good resistance to dry chlorine and hydrogen chloride
•good mechanical properties at sub-zero, room and elevated temperatures
Inconel 600 Alloy is recommended for service above 700 ℃ because of its higher creep-rupture properties, obtained via controlled carbon content and, except for strip products, coarse grain size.

Density: 8.42
Corrosion resistance

Inconel 600 Alloy is resistant to a wide range of corrosive media. Due to the chromium content the alloys possess better corrosion resistance than Nickel 200/201under oxidizing conditions.
At the same time, the high nickel content results in good corrosion resistance under reducing conditions and in alkaline solutions and leads to virtual immunity to chloride-ion stresscorrosion cracking.
Inconel 600 Alloy shows moderate resistance to mineral acids and good resistance to acetic, formic, stearic and other organic acids.
Excellent resistance is shown in high purity water, as used in the primary and secondary circuits of some nuclear reactors.
Inconel 600 Alloy is particularly resistant to attack by dry chlorine or hydrogen chloride, even at temperatures up to 650℃.
At high temperatures in air the soft-annealed and solutionannealed alloys show good resistance to oxide scaling and have high strength.
The alloys also resist ammonia bearing atmospheres, as well as nitrogen and carburizing gases. Under alternating oxidizing and reducing conditions the the alloys may suffer from selective oxidation (green rot).

Applications of Inconel 600:

Typical applications are:

•thermocouple sheathing in aggresive atmospheres
•vinylchloride monomer production: resistance to chlorine,
hydrogen chloride, oxidation and carburization
•conversion of uranium oxide to hexafluoride: resistance to attack by hydrogen fluoride
•production and use of caustic alkalis, particularly in the
presence of sulphur compounds
•production of titanium dioxide by the chlorine route
•production of organic and inorganic chlorinated and fluorinated compounds: resistance to attack by chlorine and fluorine
•nuclear reactor components
•heat treatment furnace retorts, furnace belts and components, particularly with carburizing or nitriding atmospheres
•catalyst regenerators in petrochemical production

Chemical composition

 Ni  Cr  Fe  C  Mn  Si  Cu  Mo  Ti  B  P  S
 min(%)  bla  14.0  6.0
 max(%)  17.0  10.0  0.15  1.00  0.5  0.5  0.03  0.015

Mechanical properties

    Condition  Yield Strength(Mpa)  Tensile Strength(Mpa)  Elongation(%)  Hardness(HB)
 ASTM Min Value  Soft Annealed  205  550  30  
 Typical Values at RT  Hot Worked  431  706  38  180
 Typical Values at RT  Cold Worked  706  882  20  235
 Typical Values at RT  Soft Annealed  284  608  45 145

International Specification Comparison chart

 Material  Round Bar  Plate  Pipe
 Seamless  Welded
 ASTM  UNS
N06600
 B166  B168  B167  B163/516/517
 ASME  SB166  SB168  SB167  SB163/516/517
 JIS  NCF600  H4553  G4901  H4552
 DIN  2.4816  17752  17750  17751

Product: Sheet, Coil, Pipe, Bar, Wire and Forgings