Common corrosion forms of titanium alloy

Titanium alloy

Titanium alloy has a low density, high strength, corrosion resistance, good process performance, etc., it is ideal aerospace engineering (34.27, 0.85, 2.54%) structural materials. In the actual production environment, different types of corrosion will occur, Detect-Metals will introduce the common corrosion forms of titanium alloy, mainly the following categories:

1, crevice corrosion

Gaps in metal structures or defects, due to the stagnation of the electrolyte constitute an electrochemical cell and cause localized corrosion in neutral and acidic solution, contact corrosion occurs at the gap is much greater than the probability of titanium alloy alkaline solution, contact corrosion does not occur Throughout the slit surface, but eventually lead to local perforation damage.

2, pitting

In most titanium salt solution without pitting, which occurred in a non-aqueous solution and high boiling concentrated chloride solution, the solution of halide ions on the surface of the passivation film is etched titanium, titanium internal diffusion to occur pitting , pitting diameter less than its depth. Some organic medium and titanium alloy pitting phenomenon will occur in the halogen solution, titanium alloy pitting halogen solution generally occurs at high concentrations high temperature environment, in addition, sulfide and chloride pitting require specific conditions and limited.

3, hydrogen embrittlement

Hydrogen embrittlement (HE), also known as hydrogen induced cracking or hydrogen damage, is one of the early damage Failure titanium alloy, titanium and titanium alloy surface passivation film has a high intensity, sensitive to hydrogen embrittlement increases with the intensity increases, the passivation film is sensitive to hydrogen embrittlement.

4, contact corrosion

Titanium oxide surface passivation film of titanium alloy potential toward a positive potential to promote and improve the corrosion resistance of titanium acid and aqueous medium. Due to the high potential of the titanium surface, it will inevitably result in the formation of other metals in contact with an electrochemical circuit caused by contact corrosion. Titanium alloy prone to contact corrosion in the following types of media: the first is water, saline solution, water, air, HNO3, acetic acid, etc., stable electrode potential of the solution Cd, Zn, Al is more negative than Ti, anode corrosion 6 to 60 times the rate of proliferation of said second type is H2SO4, HCl, etc., Ti in these solutions may be in the passive state, it may be in the activation state, the actual contact corrosion is common during the first class solution corrosion. Usually anodized layer on the substrate surface modified form, hindering contact corrosion.

 

5 Tips you need to learn before welding aluminum

welding aluminum
Preweld cleaning requires two operations: oil/grease removal and oxide removal. As below, remove oils and greases first, then remove the oxide. Don’t reverse this order.

Take the following 5 tips before welding aluminum:

1. Remove oil, grease, and water vapor using an organic solvent such as acetone or a mild alkaline solution like a strong soap. You may also use citrus-based degreasers, but be sure to rinse and dry the part before welding.
2. Remove surface oxides with a stainless steel wire brush (used only for aluminum) or strong alkaline or acid. Many welding suppliers sell oxide-removal solutions in spray or squeeze bottles for local application. Exercise extreme care when handling these solutions, and again, rinse and dry the part before welding.

3. Assemble the joint. If it won’t be welded immediately, cover the joint with brown Kraft paper to prevent dirt and grit in the air from getting into the joint.

4. Keep the aluminum dry and at room temperature.

5. Weld within a few days. Clean the joint again if it isn’t welded within that time.

More skill about aluminum metal, welcome to our site.

where to buy aluminum plate?

where to buy aluminum plate

If you want to buy aluminum plate, you maybe search online firstly. Actually, there is a building materials market in every city, but maybe it’s far and difficult to find. So where to buy aluminum plate? Let me tell you.

Since the development of global electronic commerce is so quickly, more and more people buy things whatever they want online, they can get it. Such as clothes, shoes, fruit, sofa, bed, phone, even aluminum plate and so on. We will never be worries about we can’t buy something we want. We can also buy things overseas, Courier will deliver to your hands.

You can find cheapest aluminum plate price online, you have more choice to know suppliers from everywhere. There are many many aluminum plate for sale online.

We need to enjoy the convenience, but also to ensure the quality, so we need to be careful when buying, because there are many risks of online shopping, product is not good, you want to return, some businesses will choose to let you bear the return freight, it will deduct the transaction amount, you can buy a shipping insurance, if you are not satisfied with the product after such subject can return at any time, also free shipping, before the payment we keep good business communication, but also to keep the relevant conversations, this can prevent some deceptive behavior.

Finally, whether to buy aluminum plate or in reality purchase, choose reliable suppliers is the most important, a professional supplier can offer high quality, at the same time , provide the most professional services, because they have a reputation and praise degree, these are related to their professional services and product quality-related.

Don’t just focus on the price, ignore the quality.  Where to buy aluminum plate with cheap price and high quality?

Detect-Metals is a company that has proven experience, certified quality and dependable service providing specialty metals leadership and supply chain innovation. It is through those strengths that we have expanded abilities and supported customers for over 10 years. Customers depend on Detect-Metals for the very best in specialty metals, complete processing services, timely delivery and expert service. Detect-Metals are also the best source for providing innovative supply chain solutions worldwide.

 

How to calculate aluminum plate weight?

when you want to buy some aluminum plate,you need to pay by aluminum plate weight,but do you know how to calculate aluminum plate weight?

Actually,it’s really easy to calculate aluminum plate weight.

1.Make sure the unit of length when accounting

2.Accounting aluminum plate volume : V = length * width * thickness

3.Accounting aluminum plate weight :G = density of aluminum plate * Volume

Aluminum plate have two categories: pure aluminum(1 series of aluminum) and aluminum alloy.

The density of pure aluminum plate is 2.71 T / cubic meter (g / cc).

Aluminum alloy is divided into a number of series, commonly used for the 3 Series, 5 Series.

The density of 3 Series aluminum plate is 2.73 T / cubic meter (g / cc). The density of 5 Series aluminum plate is 2.68 T / cubic meter (g / cc).

For examp, How to calculate the 1060 aluminum plate weight : length 1 m * width 800mm * thickness 3.0mm ?

V =1000*800*3=2400000(mm)=2400(cm)

G =V*2.71=2400(cm)*2.71(g/cc)=6504g=6.5KG

Detect-Metals tell you the detailed steps about how to calculate aluminum plate weight,the leading supplier of aluminum plate for sale ,provide the best quality service.

 

what is aluminum?

what is aluminum

Aluminium is the most widely used non-ferrous metal. Global production of aluminium in 2005 was 31.9 million tonnes. It exceeded that of any other metal except iron (837.5 million tonnes). Forecast for 2012 is 42–45 million tonnes, driven by rising Chinese output.

Since Aluminium is in our life evrywhere, what is aluminum?

Aluminium is a relatively soft, durable, lightweight, ductile and malleable metal with appearance ranging from silvery to dull gray, depending on the surface roughness. It is nonmagnetic and does not easily ignite. A fresh film of aluminium serves as a good reflector (approximately 92%) of visible light and an excellent reflector (as much as 98%) of medium and far infrared radiation. The yield strength of pure aluminium is 7–11 MPa, while aluminium alloys have yield strengths ranging from 200 MPa to 600 MPa. Aluminium has about one-third the density and stiffness of steel. It is easily machined, cast, drawn and extruded.

Substance use depends on the nature of the substance. Since aluminum has a variety of excellent performance, and therefore has a very wide range of uses aluminum. What is aluminum?

Daily application:
* The quality of light aluminum alloy and high strength, which in the manufacture of aircraft, cars, rockets are widely used.

* Since aluminum has good electrical conductivity and thermal resistance, it can be used as ultra-high voltage cable materials. High purity aluminum has better performance.

* Aluminum at high temperatures highly reductive, can be used to smelt high melting point metal.

* Aluminum rich malleable, can be made of aluminum foil, used in packaging.

* Aluminum is a metal, it can be recycling, but the recovery rate is not high.

* Aluminum corrosion resistance (especially oxidized aluminum oxide because of its heat resistance but increased corrosion of aluminum) is excellent, the appearance of texture is good, affordable, it is the last election material computer chassis.

After the introduce of applications for aluminum, we also need to know its hazards. What is aluminum?

Improper use of aluminum also have some side effects:
Aluminum could result in memory loss.
Aluminum elements can damage a person’s brain cells, World Health Organization provisions of human daily intake of aluminum should be controlled at 0.004 g or less.

Detect-Metals tell you what is aluminum,and offers best aluminum with best price.

How many 6061 aluminum properties do you know?

6061 Aluminum Plate

6061 aluminum alloy as the main alloying elements of magnesium and silicon, with moderate strength, good corrosion resistance, weldability, oxidation is better. Widely used requires a certain strength and high corrosion resistance of various industrial structures, such as the manufacture of trucks, tower buildings, ships, trams, railway vehicles, furniture and so on.

6061, a cold finished aluminum wrought product, for against corrosion, oxidation and demanding applications. Good use, the interface characteristics of good and easy coating, good processability. It can be used for low pressure ammunition and aerospace connectors.

Since there are so many application of 6061 aluminum alloy,How many 6061 aluminum properties do you know?

6061 aluminum mechanical properties:

Ultimate tensile strength: 124 MPa
Tensile yield strength: 55.2 MPa
Elasticity: 68.9 GPa
Bending Ultimate Strength: 228 MPa
Bending Yield Strength: 103 MPa

6061 aluminum processing properties:

After heat-treated pre-stretching process (-T651) 6061  aluminum alloy , although its strength can not be compared with the 2XXX or 7XXX Department, but its magnesium alloy of silicon and more, with excellent processing performance, excellent welding characteristics and plating , good corrosion resistance, high toughness and processing after deformation, densification defect-free and easy to polishing, color film is easily oxidized with excellent results and other excellent features.

After a detailed introduction of Detect-Metals, I think you should very understand 6061 aluminum properties.

 

 

How to cut thick aluminum sheet?

thick aluminum sheet      aluminum sheet

Do you know how to cut thick aluminum sheet? what is thick aluminum sheet? Thick aluminum sheet refers to aluminum plates thicker than 3 mm. Thick aluminum plate divided into special thick aluminum and the thick aluminum. Special thick aluminum is the thickness of not less than 50 mm of aluminum. Special thick aluminum is mainly used in shipbuilding, boiler, pressure vessel housing beams and the like.

Thick aluminum plate and aluminum sheet metal is substantially the same. In all aspects of products, in addition to aluminum bridge, aluminum boiler, automobile manufacturing aluminum, aluminum pressure vessel and other varieties of multi-layer aluminum pressure vessel is purely slab outside, some species such as automobile frames aluminum (thickness of 2.5 to 10 mm), the pattern aluminum (thickness of 2.5 to 8 mm), stainless aluminum, heat-resistant aluminum sheet and other varieties of the same cross.

So how to cut thick aluminum sheet? There are two nice methods here:

1- flame cutting, cheap and fast, but cutting precision aluminum susceptible to bias and uneven heat deformation.

2- waterknife cutting, more expensive, speed is relatively slow, the accuracy is not very bad, basically negative 2mm.(The so-called “water knife”, is sealed with a high-pressure pump the water pressure through a nozzle made of very fine nozzle advanced carbide, sapphire, diamond and other discharge, cutting material. Some water also joined a number of long-chain polymers, such as polyethylene oxide, increased water “viscosity”.)

 

 

 

7075 aluminum plate require high strength than other aluminum plate

DSC07251

7xxx series aluminum is aluminum industry’s high-end products, 7xxx line aluminum containing mainly zinc. It belongs to the aviation series, aluminum-magnesium zinc copper alloy. Heat treatable, it is super-hard alloy, good wear resistance. 7xxx series alloys more used aircraft materials, in recent years, ski poles, golf club and other sporting goods, also used to produce this alloy.

This alloy to alloy represented 7005,7020,7075, mainly in the following three features:

One, better physical properties, compared with the 5083 aluminum plate , manufactured extruded profile is easy, workability and corrosion resistance is also good, can be obtained using the age hardening high strength; as heat treated 7075 aluminum plate, multi-T651, this treatment can be residual stress after T6 treatment, the correct and uniform stretching to prevent deformation of the workpiece during machining distortion occurs. T73 treatment, mechanical properties will be reduced, but there is a tendency to reduce the effects of stress corrosion.

Second, even the natural aging, 7xxx alloys can reach a very high strength, low sensitivity to crack;

Third, the heat-affected part of the welding, since the heating is solid melts, it later when natural aging, can restore strength, thereby increasing the strength of the welding seam. Such alloys are widely used in the manufacture of welded components.

Because 7xxx series alloys require high strength, corrosion resistance can be strong, now basically rely on imports, China’s production process to be improved.

DETECT-METALS Aluminum As the aluminum industry leader since its inception in 1997, specialized in aluminum foil production and sales, has accumulated rich experience in the industry in the area. Future, Aluminum will continue to expand further, in-depth reform, and actively explore the transformation and upgrading of the aluminum industry.

Aluminum pipe weight calculation method

 

Many friends new entrants to the aluminum business scopy , it’s generally do not know the weight of aluminum pipe calculated, in fact, there is a weight aluminum pipe formula can be set, usually under the designation investigation Materials Handbook, calculated according to the proportion of the volume *  seek. as follows:

Aluminum pipe weight formula = (OD – Wall Thickness) *wall  thickness * 0.00879 * length.
Because aluminum pipe is usually an alloy. The actual weight is slightly larger than the theoretical calculation.

For Example: diameter 28mm, wall thickness 3mm, length of 2 m, what’s the weight of this 2024 aluminum pipe ?

Answer:

(Outer diameter 28mm- wall thickness 3mm) * wall thickness of 3mm * Density factor 0.00879 * length 2m = weight of 1.32 kg of aluminum tubing.
In this explanation, the number of units of the formula, please note, in practical industrial applications, outside diameter and wall thickness of the tubes are generally measured in millimeters, the outer diameter is 28 mm, wall thickness of 3 mm, The median number of conversion can be directly used, specifically to talk about is the length, in fact, we can also be converted into length mm to count, that is 2,000,000 mm 2 meters, if we used the actual calculation are used to calculate the millimeter, then the out After dividing the weight value 1,000,000 fine. This is everyone’s computing like it!

Incoloy 800H and Incoloy 825 steel components Chart

Grade Ni,min Cu Mo Fe Mn C Si
UNS N08020(Alloy 20) 32.0-38.0 3.00-4.00 2.00-3.00 - 2 0.07 1
UNS N08028(Alloy 28) 30.0-34.0 0.6-1.4 3.0-4.0 - 2.5 0.03 1
UNS N08800(Incoloy800) 30.0-35.0 0.75 - 39.5,min 1.5 0.1 1
UNS N08810(Incoloy800H 30.0-35.0 0.75 - 39.5,min 1.5 0.05-0.10 1
UNS N08811(Incoloy800HT) 30.0-35.0 0.75 - 39.5,min 1.5 0.06-0.10 1
UNS N08825(Incoloy825 38.0-46.0 1.5-3.0 2.5-3.5 22.0,min 1 0.05 0.5
Grade S Cr Al Ti P Nb Ta
UNS N08020(Alloy 20) 0.035 19.00-21.00 - - 0.045 Nb+Ta:8xC-1.00
UNS N08028(Alloy 28) 0.03 26.0-28.0 - - 0.03 - -
UNS N08800(Incoloy800) 0.015 19.0-23.0 0.15-0.60 0.15-0.60 - - -
UNS N08810(Incoloy800H 0.015 19.0-23.0 0.15-0.60 0.15-0.60 - - -
UNS N08811(Incoloy800HT) 0.015 19.0-23.0 0.15-0.60 0.15-0.60 - - -
UNS N08825(Incoloy825 0.03 19.5-23.5 0.2 0.6-1.2 - - -

 

Know something about Hastelloy C-276

Hastelloy C-276 features:
1. In the state of oxidation and reduction, for most corrosive medium has excellent corrosion resistance.
2. Excellent resistance to pitting, crevice corrosion and stress corrosion cracking.

Hastelloy C-276 metallurgical structure:
C276 is face-centered cubic lattice structure.

Hastelloy C-276 corrosion resistance:
C276 alloy is suitable for a variety of chemical process industries contain oxidation and reduction of the medium. Higher molybdenum and chromium content of the alloy can resist the erosion of chloride ions, tungsten and further improve its corrosion resistance. C276 is one of only a few can resist moisture chlorine, hypochlorite and chlorine dioxide solution of material corrosion, the alloy of high concentration of chloride salt solution with significant corrosion resistance (such as ferric chloride and chlorine copper).

Hastelloy C-276 Application field:
C276 alloy in the chemical and petrochemical fields have been widely used, such as application components and catalytic systems in chloride-containing organic compounds in contact with. Such materials are particularly suitable for use in high temperature, mixed with impurities of inorganic and organic acids (such as formic acid and acetic acid), corrosive seawater environment.

Do you totally know about Titanium Sheet?

Brands of Titanium Sheet

US brands: GR1, GR2, GR3, GR5, GR7, GR12

Russia brands: BT1-00, BT1-0, BT1-2 etc.

Domestic brands: TA0, TA2, TA3, TA5, TA6, TA7, TA9, TA10, TB2, TC1, TC2, TC3, TC4

A reference standard

1: GB 228 metal tensile test method

2: GB / T 3620.1 titanium and titanium alloys and chemical composition

3: GB / T3620.2 titanium and titanium alloy products and ingredients of the chemical composition of tolerance

4: GB 4698 sea titanium, titanium and alloy chemical analysis method

Titanium implementation of standards

GB: GB / 3621-2007, GB / T13810-2007

American Standard: ASTM B265, ASTM F136, ASTM F67, AMS4928

Titanium production specifications

T 0.5-1.0mm x W1000mm x L 2000-4000mm

T 1.0-5.0mm x W1000-1500mm x L 2000-3500mm

T 5.0- 30mm x W1000-2500mm x L 3000-6000mm

T 30- 80mm x W1000mm x L 2000mm

Titanium sheet Production Status:

Thermal processing status (R)

Cold state (Y)

Annealed condition (M)

Titanium sheet manufacturing process:

Forging metal above the recrystallization temperature forging process carried.

Rolling the hot rolling at a temperature above the recrystallization temperature.

Cold-plastic deformation temperature below the temperature of the rolling process reply.

Annealing: The metal was slowly heated to a certain temperature, maintaining a sufficient time, and then cooling at an appropriate rate (usually slow cooling, and sometimes controlled cooling) the heat treatment process of a metal.

Pickling: The article is immersed in an aqueous solution of sulfuric acid to remove the oxide film such as a metal surface. Pre-treatment or intermediate plating, enamel, rolling and other processes of treatment.

Titanium sheet features:

1. The titanium starting sheet is equivalent to the surface of the oxide film with a good durable wear hair separating agent, using a titanium plate to save the species separating agent, so that the plate peel easily, eliminating the pre-treatment process kinds plate, titanium species board lighter than copper seed plate half.

2. titanium starting sheet is more than three times the life of the copper seed plate, depending on the operating conditions of up to 10-20 years

Copper crystal structure

3. Plate Preparation titanium species dense, smooth surface, good quality.

4. As the titanium species sheet without smearing separating agent, and thus avoid contamination copper electrolyte.

5. The increase productivity to reduce copper production costs, thus better economic benefits.

How to enhance the competitiveness of aluminum sheet suppliers

The current intense competition between aluminum sheet suppliers, in order to gain market share in such a market environment and is not easy, but is not no way. For some achievements have been in the market in terms of aluminum sheet suppliers, more should be efforts to enhance competitiveness, otherwise behind.

How to enhance the competitiveness of aluminum sheet suppliers :

1. The production scale, product diversification. Due to the depreciation of production equipment is slower than the average market return excess earnings rate of return, aluminum sheet suppliers operate around the regression average return is the inevitable result, the difference between competitors is reflected in the cost control. Only good cost control, 6061 aluminum price will be more competitive.

2. The sub-sector positioning. Consumption structure and economic development structure is adapted to aluminum, aluminum factory management needs to have a forward-looking position or to emerging sub-sub-industry transformation.

3. The high capacity or capital flexibility. When the sub-sectors appear excess return, the aluminum sheet suppliers can be put into maximizing the expansion of production capacity faster than its competitors to achieve excess returns through capital efficiency, so it’s not just “industry how good” or “more than anyone else has money “, but also need to” faster than anyone else. “

6061 aluminum sheet has many valuable features

Aluminium sheet is now very extensive use of a material in which 6061 is a low-alloyed aluminum Al-Mg-Si-based alloy high plasticity, has many valuable features. Below lists the 6061 aluminum sheet with the characteristics.

1.6061 aluminum sheet welding performance and excellent corrosion resistance, no stress corrosion cracking tendency, in the heat treatment can be reinforced in aluminum alloy, Al-Mg-Si based alloy is not the only discovery of stress corrosion cracking of the alloy.

2. heat strengthened, high impact toughness of 6061 aluminum sheet, do not sensitive to lack.

3. aluminum manufacturer machined surface is very smooth, and easy to anodizing and coloring. The disadvantage is that after quenching, if parked for some time at room temperature, an adverse impact on aging (parked effect) have strength.

4.6061 aluminum sheet with excellent thermoplastic can be extruded into complex high-speed, thin-walled, hollow variety of profiles, or forged into complex forgings. Quenching temperature range, low quench sensitivity, after extrusion and forging release, as long as the temperature is higher than the quenching temperature, you can use water or through water quenching method. Thin-walled parts (δ <3mm) can also carry out air quenching.

6061 aluminum sheet has many valuable features , it is summed up 6061 aluminum sheet having excellent weldability and corrosion resistance, high impact toughness, processing surface is very smooth, with excellent thermoplastic these characteristics. These features make the 6061 aluminum sheet have obvious advantages when wholesale.

6061 aluminum plate superior performance

DSC07248

6061 aluminum plate belong to 6XXX serise alloy aluminum , the main alloying elements are magnesium and silicon. Products with moderate strength, good corrosion resistance, weldability, oxidation is better, is widely used in trucks, tower buildings, ships, trams, rail vehicles with a certain strength and high corrosion resistance of industrial structure, such as manufacturing and so on.

From the production process point of view, from 6061 alloy semi-continuous casting, homogenization, sawing, milling surface, clad, heating, hot rolling, annealing, cold rolling, annealing, cold rolling, solution treatment, aging treatment, to cut cutting, leveling, inspection, oiled packaging of this series of process, constitute a complete production step 6061 aluminum sheet .

6061 aluminum production process has been very mature now, at present, the domestic production of the factory in 6061 alloy have dozens, while Detect-Metals is one representative leader.

What is Aluminum Coil?

Aluminum coils by rolling after casting machine, pull the corners processing, For the shears metal commodities.

How many types does aluminum coils have?

Aluminum coils are widely used in electronics, packaging, construction, machinery, etc., Chinese aluminum coil production company more prosperous country has caught up the production process, on the basis of aluminum coil aluminum coil aluminum-rich metallic element is not the same, aluminum coil can roughly divide for the nine categories, that is capable of sub-nine series, the following about the gradual introduction:

1, the 1000 series: the representative of 1,050,106,010,701,000 series aluminum is also known as pure aluminum, in all series, 1000 series aluminum content attributed most of a series.

2, the 2000 series aluminum sheet: representative of 2A16 (LY16) 2A06 (LY6) 2000 series aluminum is characterized by high hardness, during which the copper-origin content, about 3-5% or so.

3, the 3000 series aluminum sheet: representative of the main 3003 3003 3A21. It can be called anti-rust aluminum China 3000 series aluminum production process is more excellent.

4, the 4000 series aluminum: representatives 4A01 4000 series aluminum attributed to higher silicon content.

5, the 5000 series: the representative 5052.5005.5083.5A05 series.

6, the 6000 series: 6061 on behalf of the first two elements are rich in magnesium and silicon, it is focused on the 4000 series and 5000 series of the strengths of 6061, a cold finished aluminum casting goods for opposition corrosion, oxidation and demanding applications.

7, 7000: 7075 on behalf of the primary zinc-rich

8, 8000 Series: more commonly attributed to other series for 8011

9, 9000: attributed to spare series, science and technology is now so prosperous, in order to respond to other alloying elements aluminum-rich presentation, the International Federation of special aluminum strip marked 9000 as the backup series, waiting for another new species to fill the 9000 presentation series blank.

how can we distinguish the fake or real aluminum alloy fastly?

Since more and more aluminum alloy products appear after another, it’s not easy to tell when we select it, a lot of unscrupulous manufacturers took the opportunity to make trouble, aluminum alloy mixed fish heads on the market, real to the enemy, indeed a headache for consumers. But how can we distinguish the fake or real aluminum alloy fastly?

1. There are two sides of aluminum alloy:sub-sided and single-sided.

2. At the time of purchasing it,you need to observe its surface and color, whether the appearance is smooth, the color is gorgeous.

3. aluminum alloy glue seam neat, decorative aluminum plate when building exterior, between the plates must usually have a slit width.

4. If the appearance of aluminum alloy with deform and dark,these are defective.

5. You can analyze aluminum alloy, the primary problem is on the bottom of the aluminum plate , the dealer would recommend that you purchase the underlying data is the high-density wood panels and more similar. It’s outdoor use, their life is very weak, will deform easily after wind, sun and rain. The underlying data are already deformed, do not be fooled by dealers, must hold what you want to buy.

How to clean pattern aluminum plate professionally?

Pattern aluminum plate in life is becoming more common, and the role of pattern aluminum is also growing, after the washing process will become more beautiful pattern aluminum alloy in the production process will often appear loose ingot or blowhole and other defects, to the production process of a lot of trouble. Following small and you a brief introduction pattern aluminum plate washing deal with it, how to be more professional washing pattern aluminum plate.

Start porosity is concerned, it is mainly among aluminum ingot circular hole, the reason is mainly formed when dissolved gas is always in a state of saturation, and the melt, there are still a lot of non-metallic inclusions It slows things, so that the gas in the process of casting floating rate, bubbles will remain in the pores of the ingot.

Loose ingot form factors are two: First, there is no removal of loose melt gases; the second is a loose contraction generated when it is related to gas and melt, generally when we conduct analysis mainly based on gas content of the melt and the casting speed.

In fact, we can also use a liquid feeding mode, so it reduces the metal in the furnace residence time, can make the inside of the gas furnace in the continuous saturation effect to get a good release and decomposition, but also good control generation of impurities, reduce non-metallic slag material.

1, after alkaline etching, the aluminum plate surface pattern will be left Dalian alkaline etching grooves film, which we call water alkaline etching after. Pattern aluminum plate base after etching is more difficult to clean, and first of all we want in favor of cleaning products point of view, the first tank to maintain the temperature of the water and alkaline water is not going to replace. After washing twice, in order to make a better cleaning effect, we can be appropriately stirred. After washing twice watching work How much amount may be, it can not handle the overflow.

2, it is necessary to go through at least two water washing step is called neutralized. This washing we recommend using circulating water cleaning, doing so in order to protect normal oxidation tank when, because in and the nitric acid tank, if it is brought into the oxidation tank, then there may not form an oxide film, or an increase in the oxidation tank impurities, this will accelerate the aging of the oxidation tank.

3, a simple two washing, washing after chemical polishing after chemical polishing will be from some residual liquid, in order to better clean, small second sink recommend using circulating water, the first water tank maintained at a temperature on the line.

Intorduce Aluminum pipe classification to you

13517e23c8dc045

Industrial pure aluminum aluminum content between 98.8-99.7%, but the pure aluminum material is too soft not have too much practical value, alloy aluminum products is based on pure aluminum group in general, the main alloying elements are copper, silicon, magnesium, zinc, manganese, minor alloying elements are nickel, iron, titanium, chromium, lithium and so on. Because of its high strength, light weight, easy processing, good appearance and corrosion-resistant properties, is used in many industries.

Aluminum alloy grades used by four digit naming alloy group ,in order to  the distinction between aluminum alloy content:

Aluminum Alloy Grade  main alloying elements
1XXX Pure Aluminum (Al content of not less than 99.00%)
2XXX Cu (Copper)
3XXX Mn (manganese)
4XXX Si (silicon)
5XXX Mg (magnesium)
6XXX Mg + Si (Mg + Si)
7XXX Zn (zinc)
8XXX Other elements

Different aluminum series grades have  differences performance  and applications , the DETECT-METALS  currently produces precision aluminum pipe primarily is  3XXX and 5XXX series, especially in 3003,3103,5049 and 5052, mostly because of its good corrosion resistance and formability, These aluminum pipes is widely used in heat exchangers. Aluminum places 6XXX series based mainly 6061,6082,6063,6005,6110, because of its high strength, easy machining, weldability and corrosion resistance, 6061 aluminum pipe extrusions used in many structural components .

How to clean stainless steel surface?

Note that scratch the surface of the washing does not occur, to avoid the use of bleach-containing composition and abrasive cleaning liquid, steel balls, grinding tools, in order to remove the washing liquid, at the end of washing, rinsing the surface with clean water.

Surface state
Washing

Easy to get rid of dust and dirt
Soap, washing detergent or weak with warm water

Labels and foil
With warm, weak detergent to scrub the adhesive composition with alcohol or an organic solvent

Fats, oils, oil pollution
With a soft cloth or paper neutral washing detergent or ammonia solution or special washing to dry after use drugs

Bleaches as well as various acids attached
Rinse immediately with ammonia or soda solution soak carbonate, after washing with neutral detergent or warm water

Organic carbide attachment
Soak in a hot neutral detergent or ammonia solution is then washed with a detergent containing weak ground

Fingerprint
With alcohol or organic solvents (diethyl ether, benzene), with a soft cloth and then washed with water

Rainbow pattern
Excessive use of detergent or oil caused by washing with warm water and mild detergent

Welding heat discoloration
With 10% nitric acid or hydrofluoric acid, ammonia or washing soda carbonate solution and then with light and handle, and then washed with water. Drugs may also be used for washing

Corrosion caused by surface contaminants
Washed with 10% nitric acid or abrasive detergents, drugs or the use of special washing